April 
Thursday, 26 April, 2012, 21:13
Posted by Piotr Drzymala
The analysis of the sample phase of titanium alloy of aluminum, titanium and niobium coated hydroxyapatite for beam angles 1, 2, 5 degrees. The first sample had a 100-nanometer layer of hydroxyapatite, while the second sample was coated with a layer of hydroxyapatite dwustudwudziesto nanometer. Sample was studied in two theta angle of twenty-five degrees to one hundred twenty degrees. The study revealed a grazing phases:
00-049-1446 (I) - Aluminum Titanium - Al3Ti - Y: 21.51% - dx by: 1 - WL: 1.78897 - Cubic - a 3.97200 - b 3.97200 - c 3.97200 - alpha 90.000 - beta 90.000 - gamma 90.000 - Primitive - Pm-3m (221) - 1 - 62.6654 - F12 = 61 (0.0090
00-042-1134 (I) - Aluminum Titanium - Al5Ti2 - Y: 22.30% - dx by: 1 - WL: 1.78897 - Tetragonal - a 3.90530 - b 3.90530 - c 29.19630 - alpha 90.000 - beta 90.000 - gamma 90.000 - Primitive - P4/mmm (123) - 4 - 445284 - F10 =
00-007-0359 (D) - Aluminum Vanadium - Al6V - Y: 16.10% - dx by: 1 - WL: 1.78897 - Hexagonal - a 7.71800 - b 7.71800 - c 17.15000 - alpha 90.000 - beta 90.000 - gamma 120.000 - Primitive - P63/mmc (194) - 8 - 884717 - F18
However, failure to identify the phases:
01-076-8436 (N) - Apatit-(CaOH) - Ca5 (PO4) 3 (OH) - Y: 35.82% - dx by: 1 - WL: 1.78897 - Hexagonal - a 9.4
01-073-1731 (I) - hydroxylapatit - Ca5 (PO4) 3 (OH) - Y: 29.97% - dx by: 1 - WL: 1.78897 - Hexagonal - a 9.40
view entry ( 230 views )   |  print article