Tuesday, 9 October, 2012, 09:27 Posted by Grazyna Kulesza
The plan set in September was carrier lifetime measurements for silicon after acid texturization. The results were inconsistent with the expected (derived from the literature) because of occurring in wafers surface recombination prevented accurate measurement. For the correct measurement it is required to passivate the surface of silicon wafer what is planned for October.
PhD report (September HK)
Monday, 8 October, 2012, 07:00 Posted by Honorata Kazimierczak
In September I’ve continued the the voltammetric studies on a copper surfaces, from stable homogeneous Zn(II)-Mo(VI) citrate baths with various concetrations of sodium citrate and sodium molybdate. The voltammetric measurements were performer in a tree-electrode cell , by means of potentiostat PARSTAT 2273 or PGSTAT302N. A copper disc was the working electrode (surface area 2.83 cm2). A platinum sheet (5cm2) was used as the counter electrode. The working electrode potentials were referred to the saturated calomel electrode (SCE) and were ohmic drop, as measured by the current interrupt method, was compensated for.
PhD report (September 2012)
Friday, 5 October, 2012, 20:50 Posted by Marta Gajewska
Last month I took part in the ”9-th Polish-Japanese Joint Seminar on Micro and Nano Analysis” (Sieniawa, 10-13.09.2012). I had an opportunity to present a poster there entitled “Microstructure and microhardness of ball milled/hot pressed aluminium with Mg3N2 addition”, which described my first attempt to produce an AlN reinforcement in situ, in an aluminium matrix (via mechano-chemical solid state reaction).
Friday, 5 October, 2012, 14:34 Posted by Piotr Bobrowski
Most of this month was spend on holidays, so there is much to write about but it does not concern science. Berore holidays i was interpreting data collected during previous month.
Friday, 5 October, 2012, 08:41 Posted by Pawel Czaja
Having researched some more literature we came up with new compositions to be studied. New alloys will cast by means of induction melting as well as arc melting. Then we will transfer the bulk alloys into melt spun ribbons in order to compare the properties resulting, if any difference, from microstructure rfeinment.