Friday, 8 November, 2013, 14:20
Posted by Katarzyna Stan
The most interesting things from this month:

-during research stay in Budapest I had opportunity to perform in-situ heating of the melt spun ribbons in TEM
- I have received positive review of my article
- I have carried out microhardness measurements of melt spun ribbons
- in order to prepare compact samples I have pulverized firs series of melt spun ribbons using vibration micro mill
- I have participated in the Joint PhD Seminar at the AGH University

view entry ( 103 views )   |  print article
October 2013/ Piotr Bobrowski 
Wednesday, 6 November, 2013, 12:26
Posted by Piotr Bobrowski
In the beginning of this month presented a seminar in the Institute of Metallurgy and Materials Science PAS. The seminar was connected with the beginning of the PhD procedure and it was entitled: “Application of three-dimensional orientation microscopy to microstructure characterization”. The supervisor of the work is Prof. dr hab. inż. Marek Faryna and the assistant supervisor is dr inż. Anna Sypień.
view entry ( 81 views )   |  print article
PhD report (October 2013) J.Poplewska 
Wednesday, 6 November, 2013, 11:33
Posted by Jagoda Poplewska
This month, I attended in a seminar called "2nd Joint PhD Seminar" held in Krakow in 17-18 October 2013. That was the second meeting of PhD students from PAS and TU Dresden (Germany) and this year also joined the semminar PhD students of AGH.

I gave a presentation: " Morphological and textural changes during annealing of fine grained AA1050 aluminum alloy ."

Summary of my presentation was published in the conference proceedings:

Abstract
The main aim of the experiment was to analyze the microstructure and texture changes during recrystallization of commercial AA1050 aluminium alloy. The samples were processed by equal channel angular pressing (ECAP) along route A up to six passes and then annealed for 1 hour at selected temperatures (ranging from 100°C to 350°C) to obtain different states of recrystallization. Studies carried out using scanning electron microscopy equipped with high-resolution electron backscattered diffraction facility (EBSD). An additional analysis was made by means of X-ray diffractometer.
The obtained results showed that at lower annealing temperatures, the material retains ultra-fine grain structure formed by ECAP.
At higher annealing temperatures rapid grain growth appears and transformation of flattened grains into nearly equiaxed ones was observed. Particular role in the rise of nuclei (at early stages of recrystallization) was attributed to migration of low-angle boundaries and cells coalescence. Later recrystallization stages were attributed to high-angle grain boundaries migration. These processes led to nearly equiaxed grains. It was documented that the length of traces of low- and high- angle boundaries decrease with increasing temperature of annealing. For lower annealing temperatures, the average values of misorientation angle across both types of grain boundaries increases. However, above the temperature of 270°C the value of misorientation angle across the low-angle boundaries decreases. The {111} pole figures showed in the deformed and partially recrystallized states two, nearly complementarily oriented texture components. At the temperature of 270°C these texture components were changed into other two dominant (also complementarily or twin-related) ones.

view entry ( 110 views )   |  print article
PhD report G. Kulesza (October'13) 
Tuesday, 5 November, 2013, 16:02
Posted by Grazyna Kulesza
I examined waviness of silicon wafers using contact profilometer. It turned out that as a result they have cut quite high inhomogeneity in thickness reaching even 8 microns. Above all, I had a presentation with all obtained results and I was able to register for Ph.D. title conferment procedure.
view entry ( 60 views )   |  print article
October 
Tuesday, 5 November, 2013, 15:46
Posted by Jakub Kawalko
In october i have attended a 4th Stanislaw Gorczyca School on TEM Basics and Advanced Sample Preparation which was organized by the AGH in Krakow. During the school I have listened to a number of lectures regarding various aspects of electron microscopy techniques and applications. Lectures were covering broad spectrum of subjects related to electron microscopy with main focus converged on Transmission Electron Microscope. Each segment was followed with practical demonstration on actual equipment, where participants had chance for more discussion regarding ways of conducting experiments.
Following the EM school i took place in 2nd Joint PhD Seminar this time organized in Krakow. During the seminar multiple oral presentations have been given by PhD students and young scientists from organizers institution (Institute of Metallurgy and Materials Science PAS and AGH Faculty of Materials Science and Ceramics) as well as from abroad (TU Dresden). During the poster session I have presented poster presentation concerning my latest results on microstructural characterization of KoBo deformed hexagonal materials. Title of the presentation was: “Microstructure characterization in hexagonal materials deformed plastically by complex loading”.
view entry ( 58 views )   |  print article